I guess it depends on whether maximum strength of the joint is important. Personally I would tig braze it then flow a high zinc content solder over it to give corrosion resistance if I was looking for maximum strength, otherwise soldering it would be the preferred method. Since you have not told exactly what it is you are making and the material thickness, type of joint etc. it is hard to determine an exact process to use.

Thurmond