Very nice what did you do to prep the joint? And why did you use 5356 im only curious i know 5356 offers alot more strength but i thought 4043 would be a little more towards this application.but it still looks excellent no porosity it must have been a hair line fracture . Thats pretty weird that the other side didnt break or crack usually cast aluminum doesnt give at all