Hybrid Tungsten?

[Wookie]

Jake, you have probably hit the nail on the head, I’m not good at post flow, not sure why, but I do indeed have a tendency to pull the torch away to quickly. I think I may have mentioned that before somewhere on here. Next time I weld I’ll try to pay attention, I’ve had others say the same thing though, so maybe inherent to the tungsten and not just my lack of patience, hard to say.
Wookie, I would also, there maybe something out there In cyberspace, it’s been a long time since anything I’ve welded has been x-rayed, but with Hf start I think some transfer is inevitable however, even with Zirconiated tungsten.

so your saying with HF start its inevitable ... i would have to disagree with you on that
with scratch start yes but not HF start