For your first time on AL that weld looks very good.

Quote:

---

Originally Posted by ShaneJackson

For your first time on AL that weld looks very good.

---

Thanks!

I turned the AC balance down to 35% as per Rambozo's post and it welds so good now! Went up to around 125hz AC frequency and I got a nice tighter cone.

Here is a pic of me playing around with the settings. Put 2x 36" filler rods into it.

http://just.razzi.me/photos/951471/19b8856.jpg

If you read our forum, you will find 120Hz and 30% is the starting range for aluminum. Maybe something for the manual if not there. But posted many time...

The first picture was not at 65% either, you would have a lot more etching.

Quote:

---

Originally Posted by everlastsupport

If you read our forum, you will find 120Hz and 30% is the starting range for aluminum. Maybe something for the manual if not there. But posted many time...

The first picture was not at 65% either, you would have a lot more etching.

---

First picture was 60-65%.